LG422 Anti-Tarnish-Sterling Silver Round Wire

Manufactured by LeachGarner, the leading mill house in the United States, this product is produced to meet the recent demand in the marketplace for sterling silver alloys that resist fire scale and also resist tarnishing so product cleans up quickly and remains bright and shiny longer than traditional sterling silver alloy goods. The LeachGarner LG422 low tarnish and fire scale resistant Sterling Silver is also brighter and harder than traditional Sterling Silver. You can use LeachGarner LG422 low tarnish and fire scale resistant sterling silver with both traditional silver and argentium silver solders. Please see Argentium Silver Wire for more wire gauge choices.

Choose from Ounces or Feet (12")

1 Ounce

    Part No.     Gauge

• 844LG-22  22 gauge (0.65mm-.025" thick, approximately 30 feet long)

12" long

    Part No.     Gauge

• 844LG-22  22 gauge (0.65mm-.025" thick)

Working Characteristics:

• Stamping-Drawing-Spinning-Rolling: Excellent
• Enameling: Poor
• Casting: Excellent

Other Features:

 

• Density: 5.36 troy ounces/in³
• Solidus: 1504^oF (818^oC)
• Liquidus: 1655^oF (902^oC)
• Annealing: The temperature range is 100^oF (538^oC) to 1200^oF (649^oC) with a dwell time ranging from 30 to 60 minutes at temperature depending on size of furnace load.
• Brazing: Material can be torch or furnace brazed.  Best results are obtained when using solders with a flow point below 1350^oF (732^oC)
• Age Hardening: LG422 may be age hardened by annealing at 1000-1200^oF (538-649^oC) for 30-60 minutes followed by a water quench.  Age at 575-650^oF (300-350^oC) for 45-60 minutes.